| 品牌 | LG |
| 货号 | 1151 |
| 用途 | 汽车领域的应用 通用 |
| 牌号 | HI1002FA HI2100M |
| 型号 | HI1002FA HI2100M |
| 品名 | PBT |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LG Chem Ltd. |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.37
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
26
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.70 to 1.1
|
%
|
ASTM D955 |
|
Water Absorption (24 hr, 23°C, 50% RH)
|
0.070
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 1 (Break)
|
68.6
|
MPa
|
ASTM D638 |
|
Tensile Elongation 1 (Break)
|
4.0
|
%
|
ASTM D638 |
|
Flexural Modulus 2 (3.20 mm)
|
3140
|
MPa
|
ASTM D790 |
|
Flexural Strength 2 (3.20 mm)
|
98.1
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 6.40 mm)
|
34
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm)
|
190
|
°C
|
ASTM D648 |
|
Peak Melting Temperature
|
223
|
°C
|
ASTM D3418 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
100 to 120
|
°C
|
|
|
Drying Time
|
4.0 to 6.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Rear Temperature
|
240 to 250
|
°C
|
|
|
Middle Temperature
|
240 to 250
|
°C
|
|
|
Front Temperature
|
240 to 250
|
°C
|
|
|
Nozzle Temperature
|
240 to 260
|
°C
|
|
|
Processing (Melt) Temp
|
223
|
°C
|
|
|
Mold Temperature
|
60 to 100
|
°C
|