| General | ||||
|
Material Status
|
|
|||
|
UL Yellow Card 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.33
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
4.0
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.90 to 1.3
|
%
|
ASTM D955 |
|
Water Absorption (24 hr, 23°C, 50% RH)
|
0.080
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield)
|
49.0
|
MPa
|
ASTM D638 |
|
Tensile Elongation 2 (Break)
|
> 50
|
%
|
ASTM D638 |
|
Flexural Modulus 3 (3.20 mm)
|
1960
|
MPa
|
ASTM D790 |
|
Flexural Strength 3 (3.20 mm)
|
72.6
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.20 mm)
|
690
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm)
|
90.0
|
°C
|
ASTM D648 |
|
Peak Melting Temperature
|
223
|
°C
|
ASTM D3418 |
|
RTI Elec
|
130
|
°C
|
UL 746B |
|
RTI Imp
|
120
|
°C
|
UL 746B |
|
RTI Str
|
120
|
°C
|
UL 746B |
| Electrical |
Nominal Value
|
|
Test Method
|
|
Arc Resistance
|
PLC 5
|
|
ASTM D495 |
|
Comparative Tracking Index (CTI) 4
|
PLC 2
|
|
UL 746A |
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.75 mm
|
V-0
|
|
|
|
1.5 mm
|
V-0
|
|
|
|
2.0 mm
|
V-0
|
|
|
|
2.3 mm
|
|
|
|
|
3.0 mm
|
|
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
90 to 110
|
°C
|
|
|
Drying Time
|
4.0 to 6.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Rear Temperature
|
250 to 260
|
°C
|
|
|
Middle Temperature
|
250 to 260
|
°C
|
|
|
Front Temperature
|
250 to 260
|
°C
|
|
|
Nozzle Temperature
|
250 to 270
|
°C
|
|
|
Mold Temperature
|
60 to 100
|
°C
|