| 品牌 | LG |
| 货号 | 1118 |
| 用途 | 电气/电子应用领域 汽车领域的应用 |
| 牌号 | TX5000B |
| 型号 | TX5000B |
| 品名 | PA66 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LG Chem Ltd. |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.08
|
g/cm3
|
ASTM D792 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress
|
|||
|
Yield
|
58.0
|
MPa
|
ISO 527-2/50 |
|
Break, 3.20 mm 1
|
62.8
|
MPa
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Break, 3.20 mm 1
|
10
|
%
|
ASTM D638 |
|
Break
|
60
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
3.20 mm 2
|
2110
|
MPa
|
ASTM D790 |
|
-- 3
|
2100
|
MPa
|
ISO 178 |
|
Flexural Strength
|
|||
|
3.20 mm 2
|
93.2
|
MPa
|
ASTM D790 |
|
-- 3
|
85.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | ||
|
-30°C
|
18
|
kJ/m2
|
|
|
23°C
|
26
|
kJ/m2
|
|
|
Notched Izod Impact (23°C, 6.40 mm)
|
200
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed
|
160
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed
|
150
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, Unannealed
|
135
|
°C
|
ASTM D648 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
100 to 120
|
°C
|
|
|
Drying Time
|
4.0 to 6.0
|
hr
|
|
|
Rear Temperature
|
260 to 290
|
°C
|
|
|
Middle Temperature
|
270 to 300
|
°C
|
|
|
Front Temperature
|
270 to 300
|
°C
|
|
|
Nozzle Temperature
|
270 to 300
|
°C
|
|
|
Processing (Melt) Temp
|
260 to 300
|
°C
|
|
|
Mold Temperature
|
50 to 100
|
°C
|