| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.27
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.80
|
g/cm3
|
ISO 60 |
|
Melt Volume-Flow Rate (MVR) (270°C/5.0 kg)
|
20
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | ||
|
Across Flow : 120°C, 2.00 mm 3
|
0.80
|
%
|
|
|
Across Flow : 250°C, 2.00 mm 4
|
0.80
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.80
|
%
|
|
|
Flow : 250°C, 2.00 mm 4
|
0.80
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.30
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.10
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
93.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
2000
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Yield, 23°C)
|
45.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Yield, 23°C)
|
3.5
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (23°C)
|
> 20
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 5 (23°C)
|
2000
|
MPa
|
ISO 178/A |
|
Flexural Stress 5
|
ISO 178/A | ||
|
23°C
|
70.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
65.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 6 (23°C)
|
5.0
|
%
|
ISO 178/A |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
15
|
kJ/m2
|
|
|
23°C
|
60
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-30°C
|
15
|
kJ/m2
|
|
|
23°C
|
50
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
100
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
75.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
115
|
°C
|
ISO 306/B120 |
|
Melting Temperature 7
|
225
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
1.0E-4
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
1.1E-4
|
cm/cm/°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Comparative Tracking Index (Solution A)
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.75 mm
|
V-0
|
|
|
|
1.5 mm
|
V-0
|
|
|
|
2.3 mm
|
5VA
|
|
|
|
Glow Wire Flammability Index
|
IEC 60695-2-12 | ||
|
0.8 mm
|
960
|
°C
|
|
|
1.5 mm
|
960
|
°C
|
|
|
3.0 mm
|
960
|
°C
|
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | ||
|
0.8 mm
|
775
|
°C
|
|
|
1.6 mm
|
775
|
°C
|
|
|
3.0 mm
|
775
|
°C
|
| Additional Information |
Nominal Value
|
|
|
|
ISO Shortname
|
ISO 20028-PBT+PC,,GFHLMPR,11-020; ISO 1043-4 FR(17)
|
|
| Injection |
Nominal Value
|
Unit
|
Test Method
|
|
Drying Temperature - Circulation Dryer
|
120
|
°C
|
|
|
Drying Time - Circulation Dryer
|
4.0 to 8.0
|
hr
|
|
|
Processing (Melt) Temp
|
240 to 260
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.00 to 0.02
|
%
|
Karl Fisher |