| 品牌 | 朗盛 |
| 货号 | 566 |
| 用途 | 电子电器应用 |
| 牌号 | T3150XF |
| 型号 | T3150XF |
| 品名 | PBT |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.77
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.85
|
g/cm3
|
ISO 60 |
|
Melt Volume-Flow Rate (MVR) (270°C/5.0 kg)
|
30
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | ||
|
Across Flow : 120°C, 2.00 mm 2
|
0.10
|
%
|
|
|
Across Flow : 280°C, 2.00 mm 3
|
0.80
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.10
|
%
|
|
|
Flow : 280°C, 2.00 mm 3
|
0.30
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
18500
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
160
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
1.5
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4 (23°C)
|
18000
|
MPa
|
ISO 178/A |
|
Flexural Stress 4 (23°C)
|
260
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 5 (23°C)
|
1.9
|
%
|
ISO 178/A |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
50
|
kJ/m2
|
|
|
23°C
|
50
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | ||
|
-30°C
|
45
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
230
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
210
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
210
|
°C
|
ISO 306/B120 |
|
Melting Temperature 6
|
225 to 260
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
1.0E-5
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
6.0E-5
|
cm/cm/°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Comparative Tracking Index (Solution A)
|
425
|
V
|
IEC 60112 |
| Additional Information |
Nominal Value
|
|
|
|
ISO Shortname
|
ISO 20028-PBT+PET,GF55,GHMR,07-190
|
|
| Injection |
Nominal Value
|
Unit
|
Test Method
|
|
Drying Temperature - Circulation Dryer
|
120
|
°C
|
|
|
Drying Time - Circulation Dryer
|
4.0 to 8.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.00 to 0.02
|
%
|
Karl Fisher |