| 品牌 | 朗盛 |
| 货号 | 558 |
| 用途 | 电子电器应用 |
| 牌号 | KU2-7317 |
| 型号 | KU2-7317 |
| 品名 | PBT |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Appearance
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.45
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.90
|
g/cm3
|
ISO 60 |
|
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)
|
18
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | ||
|
Across Flow : 120°C, 2.00 mm 3
|
0.30
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 4
|
1.9
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.30
|
%
|
|
|
Flow : 260°C, 2.00 mm 4
|
1.9
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.40
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.20
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
2500
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
40.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
15
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 5 (23°C)
|
2600
|
MPa
|
ISO 178/A |
|
Flexural Stress 5
|
ISO 178/A | ||
|
23°C
|
75.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
70.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 6 (23°C)
|
5.8
|
%
|
ISO 178/A |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
90
|
kJ/m2
|
|
|
23°C
|
140
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-40°C
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | ||
|
-30°C
|
60
|
kJ/m2
|
|
|
23°C
|
130
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
140
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
60.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
160
|
°C
|
ISO 306/B120 |
|
Melting Temperature 7
|
225
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
1.1E-4
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
1.1E-4
|
cm/cm/°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Comparative Tracking Index (Solution A)
|
600
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.75 mm
|
HB
|
|
|
|
1.5 mm
|
HB
|
|
| Additional Information |
Nominal Value
|
|
|
|
ISO Shortname
|
ISO 20028-PBT,MD17,GHMPR,09-020
|
|