Material Status
|
|
|
Literature 1
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.30
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.80
|
g/cm3
|
ISO 60 |
|
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)
|
60
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | ||
|
Across Flow : 120°C, 2.00 mm 2
|
0.30
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 3
|
1.7
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.30
|
%
|
|
|
Flow : 260°C, 2.00 mm 3
|
1.7
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.50
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.20
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
120
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
23°C
|
2720
|
MPa
|
ASTM D638 |
|
23°C
|
2800
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress
|
|||
|
Yield, 23°C
|
55.0
|
MPa
|
ISO 527-2/50 |
|
Break, 23°C
|
48.3
|
MPa
|
ASTM D638 |
|
Tensile Strain
|
|||
|
Yield, 23°C
|
8.0
|
%
|
ISO 527-2/50 |
|
Break, 23°C
|
38
|
%
|
ASTM D638 |
|
Nominal Tensile Strain at Break (23°C)
|
> 20
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
23°C
|
2380
|
MPa
|
ASTM D790 |
|
23°C 4
|
2700
|
MPa
|
ISO 178/A |
|
Flexural Strength
|
|||
|
23°C
|
89.6
|
MPa
|
ASTM D790 |
|
23°C 4
|
90.0
|
MPa
|
ISO 178/A |
|
3.5% Strain, 23°C 4
|
80.0
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 5 (23°C)
|
6.0
|
%
|
ISO 178/A |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
100
|
kJ/m2
|
|
|
23°C
|
200
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-40°C
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
160
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
60.0
|
°C
|
ISO 75-2/A |
|
Melting Temperature 6
|
225
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
1.2E-4
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
1.2E-4
|
cm/cm/°C
|
| Additional Information |
Nominal Value
|
|
|
|
ISO Shortname
|
|
|
| Injection |
Nominal Value
|
Unit
|
Test Method
|
|
Drying Temperature - Circulation Dryer
|
120
|
°C
|
|
|
Drying Time - Circulation Dryer
|
4.0 to 8.0
|
hr
|
|
|
Processing (Melt) Temp
|
250 to 260
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.00 to 0.02
|
%
|
Karl Fisher |