| 品牌 | 朗盛 |
| 货号 | 550 |
| 用途 | 电子电器应用 |
| 牌号 | KL1-7265 |
| 型号 | KL1-7265 |
| 品名 | PBT |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | |
|
Material Status
|
|
|
Literature 1
|
|
|
UL Yellow Card 2
|
|
|
Search for UL Yellow Card
|
|
|
Availability
|
|
|
Filler / Reinforcement
|
|
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.42
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.70
|
g/cm3
|
ISO 60 |
|
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)
|
25
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | ||
|
Across Flow : 120°C, 2.00 mm 3
|
0.10
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 4
|
1.2
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.10
|
%
|
|
|
Flow : 260°C, 2.00 mm 4
|
0.70
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.40
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.20
|
%
|
|
|
Viscosity Number (Reduced Viscosity)
|
102.0
|
ml/g
|
ISO 1628 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
170
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
23°C
|
5420
|
MPa
|
ASTM D638 |
|
23°C
|
6000
|
MPa
|
ISO 527-1/1 |
|
Tensile Strength (Break, 23°C)
|
105
|
MPa
|
ASTM D638, ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
3.5
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|||
|
23°C
|
3990
|
MPa
|
ASTM D790 |
|
23°C 5
|
5700
|
MPa
|
ISO 178/A |
|
Flexural Strength
|
|||
|
23°C
|
147
|
MPa
|
ASTM D790 |
|
23°C 5
|
170
|
MPa
|
ISO 178/A |
|
3.5% Strain, 23°C 5
|
160
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 6 (23°C)
|
4.2
|
%
|
ISO 178/A |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | ||
|
-30°C
|
30
|
kJ/m2
|
|
|
23°C
|
30
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-40°C
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | ||
|
-30°C
|
25
|
kJ/m2
|
|
|
23°C
|
25
|
kJ/m2
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
220
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
195
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
205
|
°C
|
ISO 306/B50 |
|
Ball Pressure Test (215°C)
|
Pass
|
|
IEC 60695-10-2 |
|
Melting Temperature 7
|
225
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | ||
|
Flow : 23 to 55°C
|
4.0E-5
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
1.2E-4
|
cm/cm/°C
|
|
|
Thermal Conductivity (23°C)
|
0.25
|
W/m/K
|
ISO 8302 |
|
RTI Elec
|
140
|
°C
|
UL 746B |
|
RTI Imp
|
125
|
°C
|
UL 746B |
|
RTI Str
|
140
|
°C
|
UL 746B |
|
Halving Interval
|
IEC 60216 | ||
|
Electric Strength
|
11.4
|
°C
|
|
|
Tensile Impact Strength
|
9.3
|
°C
|
|
|
Tensile Strength
|
14.0
|
°C
|
|
|
Temperature Index
|
IEC 60216 | ||
|
Electric Strength, 20000 hr
|
160
|
°C
|
|
|
Tensile Impact Strength, 20000 hr
|
140
|
°C
|
|
|
Tensile Strength, 20000 hr
|
150
|
°C
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
> 1.0E+15
|
ohms
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
> 1.0E+15
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
25
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | ||
|
23°C, 100 Hz
|
3.60
|
|
|
|
23°C, 1 MHz
|
3.50
|
|
|
|
Dissipation Factor
|
IEC 60250 | ||
|
23°C, 100 Hz
|
3.0E-3
|
|
|
|
23°C, 1 MHz
|
0.020
|
|
|
|
Comparative Tracking Index (Solution A)
|
300
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.75 mm
|
HB
|
|
|
|
1.5 mm
|
HB
|
|
|
|
Glow Wire Flammability Index (2.0 mm)
|
650
|
°C
|
IEC 60695-2-12 |
|
Oxygen Index 8
|
20
|
%
|
ISO 4589-2 |
| Additional Information |
Nominal Value
|
|
|
|
ISO Shortname
|
|
|
| Injection |
Nominal Value
|
Unit
|
Test Method
|
|
Drying Temperature - Circulation Dryer
|
120
|
°C
|
|
|
Drying Time - Circulation Dryer
|
4.0 to 8.0
|
hr
|
|
|
Processing (Melt) Temp
|
250 to 270
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.00 to 0.02
|
%
|
Karl Fisher |