| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
||||
|
--
|
1.18
|
--
|
g/cm3
|
ASTM D792 |
|
23°C
|
1.18
|
--
|
g/cm3
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 2577 | |||
|
Across Flow : 100°C, 3.00 mm 3
|
0.090
|
--
|
%
|
|
|
Across Flow : 270°C, 3.00 mm 4
|
0.49
|
--
|
%
|
|
|
Flow : 100°C, 3.00 mm 3
|
0.13
|
--
|
%
|
|
|
Flow : 270°C, 3.00 mm 4
|
0.53
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
6.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus
|
||||
|
23°C 5
|
3000
|
3300
|
MPa
|
ASTM D638 |
|
23°C
|
3300
|
3000
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress
|
||||
|
Yield, 23°C
|
110
|
90.0
|
MPa
|
ISO 527-2/50 |
|
Break, 23°C
|
64.8
|
55.2
|
MPa
|
ASTM D638 |
|
Tensile Strain
|
||||
|
Yield, 23°C
|
6.0
|
5.0
|
%
|
ISO 527-2/50 |
|
Break, 23°C
|
> 50
|
> 50
|
%
|
ASTM D638 |
|
Flexural Modulus
|
||||
|
23°C
|
2900
|
3300
|
MPa
|
ASTM D790 |
|
23°C 6
|
3000
|
3000
|
MPa
|
ISO 178/A |
|
Flexural Strength
|
||||
|
5.0% Strain, 23°C
|
150
|
130
|
MPa
|
ASTM D790 |
|
23°C 6
|
150
|
130
|
MPa
|
ISO 178/A |
|
3.5% Strain, 23°C 6
|
105
|
110
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 7 (23°C)
|
7.0
|
5.0
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-40°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
No Break
|
No Break
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
|
Notched Izod Impact
|
||||
|
-40°C, 3.18 mm
|
48
|
48
|
J/m
|
ASTM D256 |
|
23°C, 3.18 mm
|
80
|
59
|
J/m
|
ASTM D256 |
|
-40°C
|
< 10
|
< 10
|
kJ/m2
|
ISO 180/1A |
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
ISO 180/1A |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
||||
|
0.45 MPa, Unannealed, 3.99 mm
|
118
|
--
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed
|
115
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed, 3.99 mm
|
107
|
--
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed
|
105
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
125
|
--
|
°C
|
ISO 306/B120, ISO 306/B50 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
7.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
8.0E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+15
|
1.0E+15
|
ohms
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
1.0E+15
|
1.0E+15
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
25
|
28
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
23°C, 100 Hz
|
4.30
|
4.60
|
|
|
|
23°C, 1 MHz
|
3.80
|
4.00
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
23°C, 100 Hz
|
0.040
|
0.048
|
|
|
|
23°C, 1 MHz
|
0.090
|
0.11
|
|
|
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
0.75 mm
|
V-2
|
--
|
|
|
|
1.5 mm
|
V-2
|
--
|
|
|
|
Glow Wire Flammability Index (2.0 mm)
|
960
|
--
|
°C
|
IEC 60695-2-12 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
260 to 280
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |