| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.72
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.75
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 3
|
0.060
|
--
|
%
|
|
|
Across Flow : 280°C, 2.00 mm 4
|
0.46
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.020
|
--
|
%
|
|
|
Flow : 280°C, 2.00 mm 4
|
0.28
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
3.6
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.1
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
255
|
155
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
20500
|
13100
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
230
|
150
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
2.4
|
3.1
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 5 (23°C)
|
20000
|
13100
|
MPa
|
ISO 178/A |
|
Flexural Stress 5 (23°C)
|
370
|
245
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 6 (23°C)
|
3.0
|
4.0
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
16
|
--
|
kJ/m2
|
|
|
23°C
|
16
|
20
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
90
|
90
|
kJ/m2
|
|
|
23°C
|
90
|
90
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
16
|
--
|
kJ/m2
|
|
|
23°C
|
16
|
20
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
80
|
80
|
kJ/m2
|
|
|
23°C
|
80
|
80
|
kJ/m2
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
220
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
213
|
--
|
°C
|
ISO 75-2/A |
|
8.0 MPa, Unannealed
|
190
|
--
|
°C
|
ISO 75-2/C |
|
Vicat Softening Temperature
|
210
|
--
|
°C
|
ISO 306/B120 |
|
Melting Temperature 7
|
221
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
1.2E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.5E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Volume Resistivity (23°C)
|
5.8E+14
|
8.0E+11
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
33
|
33
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
23°C, 100 Hz
|
5.30
|
11.2
|
|
|
|
23°C, 1 MHz
|
4.70
|
5.10
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
23°C, 100 Hz
|
0.016
|
0.21
|
|
|
|
23°C, 1 MHz
|
0.018
|
0.065
|
|
|
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,GF60,GHR,S10-220
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
|
Residual Moisture Content
|
0.05 to 0.15
|
%
|
Karl Fisher |