| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.14
|
--
|
g/cm3
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 3
|
0.11
|
--
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 4
|
1.2
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.42
|
--
|
%
|
|
|
Flow : 260°C, 2.00 mm 4
|
1.1
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
151
|
70.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
3500
|
1400
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Yield, 23°C)
|
94.0
|
55.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Yield, 23°C)
|
4.2
|
20
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (23°C)
|
10
|
160
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 5 (23°C)
|
3200
|
1300
|
MPa
|
ISO 178/A |
|
Flexural Stress 5
|
ISO 178/A | |||
|
23°C
|
127
|
49.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
105
|
36.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 6 (23°C)
|
6.2
|
8.0
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
15
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
120
|
190
|
kJ/m2
|
|
|
23°C
|
110 kJ/m2
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
110
|
130
|
kJ/m2
|
|
|
23°C
|
80 kJ/m2
|
No Break
|
|
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | |||
|
-30°C, Total Penetration Energy
|
5.10
|
--
|
J
|
|
|
23°C, Total Penetration Energy
|
13.1
|
27.2
|
J
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | |||
|
-30°C
|
2400
|
--
|
N
|
|
|
23°C
|
3730
|
4630
|
N
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
210
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
75.0
|
--
|
°C
|
ISO 75-2/A |
|
8.0 MPa, Unannealed
|
60.0
|
--
|
°C
|
ISO 75-2/C |
|
Vicat Softening Temperature
|
> 230
|
--
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (249°C)
|
Pass
|
--
|
|
IEC 60695-10-2 |
|
Melting Temperature 7
|
265
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
7.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
9.0E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Comparative Tracking Index
|
IEC 60112 | |||
|
Solution A
|
600
|
--
|
V
|
|
|
Solution B
|
400
|
--
|
V
|
|
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
0.75 mm
|
V-2
|
--
|
|
|
|
1.5 mm
|
V-2
|
--
|
|
|
|
Glow Wire Flammability Index
|
IEC 60695-2-12 | |||
|
0.75 mm
|
960
|
--
|
°C
|
|
|
1.5 mm
|
960
|
--
|
°C
|
|
|
3.0 mm
|
960
|
--
|
°C
|
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | |||
|
0.75 mm
|
775
|
--
|
°C
|
|
|
1.5 mm
|
775
|
--
|
°C
|
|
|
3.0 mm
|
775
|
--
|
°C
|
|
|
Oxygen Index 8
|
30
|
--
|
%
|
ISO 4589-2 |
|
Burning Behavior - US FMVSS302 (> 1.00 mm)
|
passed
|
--
|
|
ISO 3795 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 66,,FR(30),GF2HR,S14-030
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
260 to 270
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Admissible Residence Time at Tmax
|
< 5.0
|
min
|
|
|
Residual Moisture Content
|
0.03 to 0.07
|
%
|
Karl Fisher |