| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.08
|
--
|
g/cm3
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 2
|
0.30
|
--
|
%
|
|
|
Across Flow : 280°C, 2.00 mm 3
|
1.7
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.40
|
--
|
%
|
|
|
Flow : 280°C, 2.00 mm 3
|
1.9
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
1850
|
650
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Yield, 23°C)
|
48.0
|
30.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Yield, 23°C)
|
15
|
35
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (23°C)
|
60
|
--
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 4 (23°C)
|
1800
|
700
|
MPa
|
ISO 178/A |
|
Flexural Stress 4
|
ISO 178/A | |||
|
23°C
|
70.0
|
30.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
55.0
|
20.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
7.0
|
7.0
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
20
|
20
|
kJ/m2
|
|
|
23°C
|
80
|
100
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
No Break
|
No Break
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
20
|
20
|
kJ/m2
|
|
|
23°C
|
75
|
100
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
No Break
|
No Break
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | |||
|
-30°C, Total Penetration Energy
|
43.4
|
40.7
|
J
|
|
|
23°C, Total Penetration Energy
|
44.0
|
37.5
|
J
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | |||
|
-30°C
|
6150
|
6100
|
N
|
|
|
23°C
|
5430
|
4500
|
N
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
140
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
60.0
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
195
|
--
|
°C
|
ISO 306/B120 |
|
Melting Temperature 6
|
262
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
1.5E-4
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
1.3E-4
|
--
|
cm/cm/°C
|
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 66-I,,GHR,S12-020
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 90
|
°C
|
|
|
Admissible Residence Time at Tmax
|
> 10.0
|
min
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |