| 品牌 | 朗盛 |
| 货号 | 351 |
| 用途 | 电子电器应用 |
| 牌号 | DP1100/30H2.0 901510 |
| 型号 | DP1100/30H2.0 901510 |
| 品名 | PA6 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.35
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.80
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 2577 | |||
|
Across Flow : 120°C, 3.00 mm 2
|
0.30
|
--
|
%
|
|
|
Across Flow : 280°C, 3.00 mm 3
|
1.1
|
--
|
%
|
|
|
Flow : 120°C, 3.00 mm 2
|
0.30
|
--
|
%
|
|
|
Flow : 280°C, 3.00 mm 3
|
1.1
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.2
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
175
|
65.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
4400
|
1350
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
70.0
|
35.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
4.5
|
150
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4 (23°C)
|
4000
|
1200
|
MPa
|
ISO 178/A |
|
Flexural Stress 4
|
ISO 178/A | |||
|
23°C
|
120
|
45.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
115
|
30.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
5.0
|
7.5
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
30
|
30
|
kJ/m2
|
|
|
23°C
|
35
|
170
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
30
|
25
|
kJ/m2
|
|
|
23°C
|
30
|
170
|
kJ/m2
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
180
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
75.0
|
--
|
°C
|
ISO 75-2/A |
|
8.0 MPa, Unannealed
|
50.0
|
--
|
°C
|
ISO 75-2/C |
|
Vicat Softening Temperature
|
205
|
--
|
°C
|
ISO 306/B120 |
|
Melting Temperature 6
|
220
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
8.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
8.0E-5
|
--
|
cm/cm/°C
|
| Flammability |
Dry
|
Conditioned
|
|
Test Method
|
|
Burning Behavior - US FMVSS302
|
passed
|
--
|
|
ISO 3795 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,GB30,GHR,S14-040
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |