| 品牌 | 朗盛 |
| 货号 | 336 |
| 用途 | 电子电器应用 |
| 牌号 | BTC965FM30 |
| 型号 | BTC965FM30 |
| 品名 | PA6 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.73
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.80
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 3
|
0.10
|
--
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 4
|
0.50
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 3
|
0.10
|
--
|
%
|
|
|
Flow : 260°C, 2.00 mm 4
|
0.60
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
3.2
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.0
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
13100
|
6700
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
75.0
|
45.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
0.70
|
1.2
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 5 (23°C)
|
14200
|
6200
|
MPa
|
ISO 178/A |
|
Flexural Stress 5 (23°C)
|
130
|
65.0
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 6 (23°C)
|
1.2
|
1.8
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Unnotched Impact Strength (23°C)
|
9.0
|
9.0
|
kJ/m2
|
ISO 179/1eU |
|
Unnotched Izod Impact Strength (23°C)
|
10
|
10
|
kJ/m2
|
ISO 180/1U |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
160
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
212
|
--
|
°C
|
ISO 306/B120 |
|
Melting Temperature 7
|
220
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
4.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
5.0E-5
|
--
|
cm/cm/°C
|
|
|
Thermal Conductivity
|
ISO 22007-4 | |||
|
-- 8
|
1.3
|
--
|
W/m/K
|
|
|
-- 9
|
2.5
|
--
|
W/m/K
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
3.8E+15
|
--
|
ohms
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
5.3E+15
|
--
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
34
|
--
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
23°C, 100 Hz
|
4.80
|
--
|
|
|
|
23°C, 1 MHz
|
4.40
|
--
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
23°C, 100 Hz
|
0.017
|
--
|
|
|
|
23°C, 1 MHz
|
0.014
|
--
|
|
|
|
Comparative Tracking Index (CTI) 10
|
PLC 0
|
--
|
|
UL 746A |
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
0.75 mm
|
V-0
|
--
|
|
|
|
1.5 mm
|
|
--
|
|
|
|
Glow Wire Flammability Index
|
IEC 60695-2-12 | |||
|
0.75 mm
|
960
|
--
|
°C
|
|
|
1.5 mm
|
960
|
--
|
°C
|
|
|
3.0 mm
|
960
|
--
|
°C
|
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | |||
|
0.75 mm
|
750
|
--
|
°C
|
|
|
1.5 mm
|
750
|
--
|
°C
|
|
|
3.0 mm
|
800
|
--
|
°C
|
|
|
Oxygen Index 11
|
> 100
|
--
|
%
|
ISO 4589-2 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,MD68 FR(61),GF2HR,S12-140
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
260 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |