品牌 | 朗盛 |
货号 | 333 |
用途 | 电子电器应用 |
牌号 | BTC65H3.0EF 901510 |
型号 | BTC65H3.0EF 901510 |
品名 | PA6 |
外形尺寸 | 25kg/包 |
生产企业 | LANXESS GmbH |
是否进口 | 是 |
General | ||||
Material Status
|
|
|||
Literature 1
|
|
|||
Search for UL Yellow Card
|
|
|||
Availability
|
|
|||
Filler / Reinforcement
|
|
|||
Additive
|
|
|||
Features
|
|
|||
Processing Method
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density (23°C)
|
2.01
|
--
|
g/cm3
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow : 120°C, 2.00 mm 2
|
0.15
|
--
|
%
|
|
Across Flow : 290°C, 2.00 mm 3
|
0.75
|
--
|
%
|
|
Flow : 120°C, 2.00 mm 2
|
0.15
|
--
|
%
|
|
Flow : 290°C, 2.00 mm 3
|
0.70
|
--
|
%
|
|
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
3.4
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
1.0
|
--
|
%
|
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
9900
|
3500
|
MPa
|
ISO 527-1/1 |
Tensile Stress (Break, 23°C)
|
90.0
|
50.0
|
MPa
|
ISO 527-2/5 |
Tensile Strain (Break, 23°C)
|
3.0
|
5.0
|
%
|
ISO 527-2/5 |
Flexural Modulus 4 (23°C)
|
10000
|
3800
|
MPa
|
ISO 178/A |
Flexural Stress 4
|
ISO 178/A | |||
23°C
|
160
|
75.0
|
MPa
|
|
3.5% Strain, 23°C
|
155
|
70.0
|
MPa
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
3.6
|
4.0
|
%
|
ISO 178/A |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
25
|
20
|
kJ/m2
|
|
23°C
|
45
|
35
|
kJ/m2
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
-30°C
|
25
|
20
|
kJ/m2
|
|
23°C
|
35
|
25
|
kJ/m2
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
190
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
145
|
--
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
208
|
--
|
°C
|
ISO 306/B120 |
Melting Temperature 6
|
221
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
ISO 11359-2 | |||
Flow : 23 to 55°C
|
5.0E-5
|
--
|
cm/cm/°C
|
|
Transverse : 23 to 55°C
|
6.0E-5
|
--
|
cm/cm/°C
|
|
Thermal Conductivity
|
ISO 22007-4 | |||
-- 7
|
1.0
|
--
|
W/m/K
|
|
-- 8
|
1.3
|
--
|
W/m/K
|
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity
|
6.0E+13
|
--
|
ohms
|
IEC 60093 |
Volume Resistivity (23°C)
|
1.0E+17
|
--
|
ohms·cm
|
IEC 60093 |
Electric Strength (23°C, 1.00 mm)
|
37
|
35
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating (0.75 mm)
|
HB
|
--
|
|
UL 94 |
Glow Wire Flammability Index
|
IEC 60695-2-12 | |||
0.75 mm
|
900
|
--
|
°C
|
|
1.5 mm
|
960
|
--
|
°C
|
|
3.0 mm
|
960
|
--
|
°C
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | |||
0.75 mm
|
750
|
--
|
°C
|
|
1.5 mm
|
750
|
--
|
°C
|
|
3.0 mm
|
750
|
--
|
°C
|
|
Burning Behavior - US FMVSS302 (> 1.00 mm)
|
passed
|
--
|
|
ISO 3795 |
Additional Information |
Dry
|
Conditioned
|
|
|
ISO Shortname
|
ISO 16396-PA 6,MD65,GHR,S10-090
|
--
|
|
Injection |
Dry
|
Unit
|
Test Method
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
Processing (Melt) Temp
|
280 to 300
|
°C
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |