| 品牌 | 朗盛 |
| 货号 | 332 |
| 用途 | 电子电器应用 |
| 牌号 | BM430H2.0 901510 |
| 型号 | BM430H2.0 901510 |
| 品名 | PA6 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.37
|
--
|
g/cm3
|
ISO 1183 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 2
|
0.20
|
--
|
%
|
|
|
Across Flow : 280°C, 2.00 mm 3
|
1.1
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.30
|
--
|
%
|
|
|
Flow : 280°C, 2.00 mm 3
|
1.2
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.1
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
4700
|
1450
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
70.0
|
35.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
5.0
|
> 100
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4 (23°C)
|
4500
|
1590
|
MPa
|
ISO 178/A |
|
Flexural Stress 4
|
ISO 178/A | |||
|
23°C
|
120
|
48.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
115
|
35.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
5.0
|
7.8
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
60
|
50
|
kJ/m2
|
|
|
23°C
|
75 kJ/m2
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
50
|
55
|
kJ/m2
|
|
|
23°C
|
65 kJ/m2
|
No Break
|
|
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | |||
|
-30°C, Total Penetration Energy
|
1.50
|
--
|
J
|
|
|
23°C, Total Penetration Energy
|
2.50
|
--
|
J
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | |||
|
-30°C
|
820
|
--
|
N
|
|
|
23°C
|
1400
|
--
|
N
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
175
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
75.0
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 6
|
222
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
8.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.0E-5
|
--
|
cm/cm/°C
|
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,MD30,GHR,S14-040
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |