| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.36
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.80
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 2
|
0.20
|
--
|
%
|
|
|
Across Flow : 280°C, 2.00 mm 3
|
0.65
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.10
|
--
|
%
|
|
|
Flow : 280°C, 2.00 mm 3
|
0.45
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
7.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.2
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
190
|
--
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
6500
|
2900
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
110
|
60.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
3.0
|
20
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4 (23°C)
|
6400
|
3000
|
MPa
|
ISO 178/A |
|
Flexural Stress 4
|
ISO 178/A | |||
|
23°C
|
180
|
100
|
MPa
|
|
|
3.5% Strain, 23°C
|
175
|
80.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
4.0
|
7.5
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-40°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
30
|
35
|
kJ/m2
|
|
|
23°C
|
35
|
110
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | |||
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
30
|
30
|
kJ/m2
|
|
|
23°C
|
30
|
95
|
kJ/m2
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
210
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
190
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
> 200
|
--
|
°C
|
ISO 306/B120 |
|
Melting Temperature 6
|
220
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
4.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
9.0E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Comparative Tracking Index (Solution A)
|
425
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating (1.5 mm)
|
HB
|
--
|
|
UL 94 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,(GF+MD)30,GHR,S10-060
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
270 to 290
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |