| 品牌 | 朗盛 |
| 货号 | 325 |
| 用途 | 电子电器应用 |
| 牌号 | BM25FN20 000000 DUS013 |
| 型号 | BM25FN20 000000 DUS013 |
| 品名 | PA6 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density (23°C)
|
1.43
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.70
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow : 120°C, 2.00 mm 2
|
0.20
|
--
|
%
|
|
|
Across Flow : 260°C, 2.00 mm 3
|
0.90
|
--
|
%
|
|
|
Flow : 120°C, 2.00 mm 2
|
0.20
|
--
|
%
|
|
|
Flow : 260°C, 2.00 mm 3
|
0.90
|
--
|
%
|
|
|
Water Absorption (Saturation, 23°C)
|
6.7
|
--
|
%
|
ISO 62 |
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
178
|
70.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
5700
|
2100
|
MPa
|
ISO 527-1/1 |
|
Tensile Stress (Break, 23°C)
|
80.0
|
30.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Strain (Break, 23°C)
|
3.0
|
7.0
|
%
|
ISO 527-2/5 |
|
Flexural Modulus 4 (23°C)
|
5500
|
2000
|
MPa
|
ISO 178/A |
|
Flexural Stress 4
|
ISO 178/A | |||
|
23°C
|
130
|
50.0
|
MPa
|
|
|
3.5% Strain, 23°C
|
130
|
43.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 5 (23°C)
|
3.3
|
6.8
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Unnotched Impact Strength (23°C)
|
38
|
140
|
kJ/m2
|
ISO 179/1eU |
|
Notched Izod Impact Strength (23°C)
|
< 10
|
< 10
|
kJ/m2
|
ISO 180/1A |
|
Unnotched Izod Impact Strength (23°C)
|
30
|
100
|
kJ/m2
|
ISO 180/1U |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
195
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
90.0
|
--
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
206
|
--
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (205°C)
|
Pass
|
--
|
|
IEC 60695-10-2 |
|
Melting Temperature 6
|
220
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
6.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.0E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Comparative Tracking Index (CTI) 7
|
PLC 1
|
--
|
|
UL 746A |
|
Comparative Tracking Index (Solution A)
|
450
|
--
|
V
|
IEC 60112 |
|
High Amp Arc Ignition (HAI)
|
|
--
|
|
UL 746A |
|
Hot-wire Ignition (HWI)
|
|
--
|
|
UL 746A |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | |||
|
0.75 mm
|
V-2
|
--
|
|
|
|
1.5 mm
|
V-2
|
--
|
|
|
|
Glow Wire Flammability Index
|
IEC 60695-2-12 | |||
|
0.8 mm
|
960
|
--
|
°C
|
|
|
1.5 mm
|
960
|
--
|
°C
|
|
|
3.0 mm
|
960
|
--
|
°C
|
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | |||
|
0.75 mm
|
725
|
--
|
°C
|
|
|
1.5 mm
|
725
|
--
|
°C
|
|
|
3.0 mm
|
725
|
--
|
°C
|
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
ISO 16396-PA 6,MD25 FR(30),GF2HR,S14-060
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
250 to 270
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.07
|
%
|
Karl Fisher |