| 品牌 | 朗盛 |
| 货号 | 322 |
| 用途 | 电子电器应用 |
| 牌号 | BM240H2.0 901510 |
| 型号 | BM240H2.0 901510 |
| 品名 | PA6 |
| 外形尺寸 | 25kg/包 |
| 生产企业 | LANXESS GmbH |
| 是否进口 | 是 |
| General | ||||
|
Material Status
|
|
|||
|
Literature 1
|
|
|||
|
UL Yellow Card 2
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
||||
|
--
|
1.46
|
--
|
g/cm3
|
ASTM D792 |
|
23°C
|
1.46
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.70
|
--
|
g/cm3
|
ISO 60 |
|
Molding Shrinkage
|
ISO 2577 | |||
|
Across Flow : 120°C, 3.00 mm 3
|
0.20
|
--
|
%
|
|
|
Across Flow : 290°C, 3.00 mm 4
|
1.2
|
--
|
%
|
|
|
Flow : 120°C, 3.00 mm 3
|
0.17
|
--
|
%
|
|
|
Flow : 290°C, 3.00 mm 4
|
1.3
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
6.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.9
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
210
|
90.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus
|
||||
|
23°C 5
|
6000
|
2000
|
MPa
|
ASTM D638 |
|
23°C
|
6000
|
2200
|
MPa
|
ISO 527-1/1 |
|
Tensile Strength
|
||||
|
Break, 23°C
|
84.8
|
50.3
|
MPa
|
ASTM D638 |
|
Break, 23°C
|
85.0
|
50.0
|
MPa
|
ISO 527-2/5 |
|
Tensile Elongation
|
||||
|
Break, 23°C
|
9.0
|
35
|
%
|
ASTM D638 |
|
Break, 23°C
|
7.0
|
40
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
||||
|
23°C
|
5400
|
1800
|
MPa
|
ASTM D790 |
|
23°C 6
|
5500
|
2100
|
MPa
|
ISO 178/A |
|
Flexural Strength
|
||||
|
23°C
|
155
|
64.8
|
MPa
|
ASTM D790 |
|
23°C 6
|
150
|
60.0
|
MPa
|
ISO 178/A |
|
3.5% Strain, 23°C 6
|
140
|
50.0
|
MPa
|
ISO 178/A |
|
Flexural Strain at Flexural Strength 7 (23°C)
|
5.0
|
8.0
|
%
|
ISO 178/A |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-40°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
|
|
23°C
|
< 10
|
12
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
90
|
90
|
kJ/m2
|
|
|
23°C
|
120 kJ/m2
|
No Break
|
|
|
|
Notched Izod Impact
|
||||
|
-40°C, 3.18 mm
|
37
|
37
|
J/m
|
ASTM D256 |
|
23°C, 3.18 mm
|
64
|
80
|
J/m
|
ASTM D256 |
|
-40°C
|
< 10
|
< 10
|
kJ/m2
|
ISO 180/1A |
|
-30°C
|
< 10
|
< 10
|
kJ/m2
|
ISO 180/1A |
|
Unnotched Izod Impact Strength
|
ISO 180/1U | |||
|
-30°C
|
75
|
85
|
kJ/m2
|
|
|
23°C
|
100 kJ/m2
|
No Break
|
|
|
|
Multi-Axial Instrumented Impact Energy
|
ISO 6603-2 | |||
|
-30°C, Total Penetration Energy
|
1.60
|
--
|
J
|
|
|
23°C, Total Penetration Energy
|
9.20
|
--
|
J
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
ISO 6603-2 | |||
|
-30°C
|
825
|
--
|
N
|
|
|
23°C
|
3050
|
--
|
N
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
||||
|
0.45 MPa, Unannealed, 3.99 mm
|
200
|
--
|
°C
|
ASTM D648 |
|
0.45 MPa, Unannealed
|
190
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed, 3.99 mm
|
105
|
--
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed
|
90.0
|
--
|
°C
|
ISO 75-2/A |
|
8.0 MPa, Unannealed
|
50.0
|
--
|
°C
|
ISO 75-2/C |
|
Vicat Softening Temperature
|
||||
|
--
|
> 200
|
--
|
°C
|
ISO 306/B120 |
|
--
|
200
|
--
|
°C
|
ISO 306/B50 |
|
Melting Temperature 8
|
222
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 55°C
|
6.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 55°C
|
7.0E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+15
|
1.0E+13
|
ohms
|
IEC 60093 |
|
Volume Resistivity (23°C)
|
1.0E+15
|
1.0E+11
|
ohms·cm
|
IEC 60093 |
|
Electric Strength (23°C, 1.00 mm)
|
35
|
38
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
23°C, 100 Hz
|
4.40
|
15.0
|
|
|
|
23°C, 1 MHz
|
4.00
|
4.70
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
23°C, 100 Hz
|
0.011
|
0.25
|
|
|
|
23°C, 1 MHz
|
0.015
|
0.10
|
|
|
|
Comparative Tracking Index (Solution A)
|
525
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Glow Wire Flammability Index (2.0 mm)
|
700
|
--
|
°C
|
IEC 60695-2-12 |
|
Oxygen Index 9
|
26
|
--
|
%
|
ISO 4589-2 |
|
Burning Behavior - US FMVSS302 (2.00 mm)
|
passed
|
--
|
|
ISO 3795 |
| Additional Information |
Dry
|
Conditioned
|
|
|
|
ISO Shortname
|
|
--
|
|
| Injection |
Dry
|
Unit
|
Test Method
|
|
Drying Temperature - Dry Air Dryer
|
80
|
°C
|
|
|
Drying Time - Dry Air Dryer
|
2.0 to 6.0
|
hr
|
|
|
Processing (Melt) Temp
|
280 to 300
|
°C
|
|
|
Mold Temperature
|
80 to 120
|
°C
|
|
|
Residual Moisture Content
|
0.03 to 0.12
|
%
|
Karl Fisher |